Synthesis and characterization of zirconium oxide modified with phosphate ion
Keywords:
Circonia, Circonia fosfatada, Método sol-gel y descomposición de 2-propanol (Zirconia, Phosphated zirconia, Sol-gel method and 2-propanol decomposition)Abstract
In this work was conducted the decomposition reaction of 2-propanol to obtain propylene using phosphated zirconia as catalyst. The synthesis of Zr(OH)4 was carried out by the sol-gel method. The materials were modified with phosphoric acid and calcined at 400°C. Characterization tests included X-ray diffraction, nitrogen physisorption, infrared spectroscopy and scanning electron microscopy. The results indicated that were obtained solids with tetragonal structure and the addition of phosphate ion increased the specific surface area in the materials. On the other hand, reaction tests revealed that the phosphated catalysts had higher catalytic activity and the active sites dominant were acid sites.References
J. Bedia, J. M. Rosas, J. Márquez, J. Rodríguez-Mirasol, T. Cordero, Carbon, 47, 286 (2009).
E. Ortiz-Islas, T. López, J. Navarrete, X. Bokhimi, R. Gómez, J. Mol. Catal. A: Chem., 228, 345 (2005).
A. M. Orlović, en: New developments in catalysis research, Ed. L. P. Bevy (Nova science publishers, New York, 2005) p. 57.
C. R. Vera, C. L. Pieck, K. Shimizu, J. M. Parera, Appl. Catal. A, 230, 137 (2002).
W. Stichert, F. Schüth, S. Kuba, H. Knözinger, J. Catal., 198, 277 (2001).
K. Arata, M. Hino, Mater. Chem. Phys., 26, 213 (1990).
L. A. Cortez Lajas, J. M. Hernández Enríquez, A. Castillo Mares, J. L. Rivera Armenta, G. Sandoval Robles, L. A. García Serrano, R. García Alamilla, Rev. Mex. Ing. Quím., 5, 321 (2006).
D. Spielbauer, G. A. H. Mekhemer, T. Riemer, M. I. Zaki, H. Knözinger, J. Phys. Chem. B, 101, 4681 (1997).
G. D. Yadav, J. J. Nair, Micropor. Mesopor. Mater., 33, 1 (1999).
A. Sayari, A. Dicko, J. Catal., 145, 561 (1994).
T. Loften, E. A. Blekkan, Appl. Catal. A, 299, 250 (2006).
G. K.Chuah, S.H. Liu, S. Jaenicke, L.J. Harrison, J. Catal., 200, 352 (2001).
Y. Ikeda, T. Sakaihori, K. Tomishige, K. Fujimoto, Catal. Lett., 66, 59 (2000).
J. M. Hernández Enríquez, L. A. Cortez Lajas, R. García Alamilla, A. Castillo Mares, G. Sandoval Robles, L. A. García Serrano, J. Alloys Compd., 483, 425 (2009).
J. M. Hernández Enríquez, L. A. García Serrano, R. García Alamilla, L. A. Cortez Lajas, A. Cueto, Superficies y Vacío, 22, 1 (2009).
J. R. Sohn, T. D. Kwon, S. B. Kim, Bull. Korean Chem. Soc., 22, 1309 (2001).
W. H. Chen, H. H. Ko, A. Sakthivel, S. J. Huang, S. H. Liu, A.Y. Lo, T. C. Tsai, S. B. Liu, Catal. Today, 116, 111 (2006).
M. Rezaei, S. M. Alavi, S. Sahebdelfar, P. Bai, X. Liu, Z. F. Yan, Appl. Catal. B, 77, 346 (2008).
J. A. Wang, M. A. Valenzuela, J. Salmones, A. Vázquez, A. García-Ruiz, X. Bokhimi, Catal. Today, 68, 21 (2001).
M. Bakos, en: Contact Catalysis, Vol. 2, Eds. Z. G. Szabó, D. Kalló (Elsevier, Amsterdam, 1976) p. 282.
G. A. H. Mekhemer, H. M. Ismail, Colloids and Surfaces A, 164, 227 (2000).
A. Gervasini, J. Fenyvesi, A. Auroux, Catal. Lett., 43, 219 (1997).
A. M. Youssef, L. B. Khalil, B. S. Girgis, Appl. Catal. A, 81, 1 (1992).
Downloads
Published
Issue
Section
License
©2025 by the authors; licensee SMCTSM, Mexico. This article is an open access article distributed under the terms and conditions of the Creative Commons Attribution license (http://creativecommons.org/licenses/by/4.0/).